In this research firstly ore characterization studies from ore dressing point of view have been conducted and then increase in module ratio i.e. ratio of Al₂O₃ to SiO₂ of the bauxite samples from Boolboolieh area of Kerman province investigated by the means of ore dressing techniques. Obtained results from ore characterization studies revealed diaspore and hematite were major mineral phases and Al₂O₃, Fe₂O₃ and SiO₂ contents of head sample were 36.6, 27.02 and 20.32 % respectively and consequently module ratio was determined to be 1.8. Mineralogical studies on all prepared microscopic sections show clastic texture that contains pisolith and oolith particles inside microcrystalline matrix formed from hematite, clay minerals and fine bauxite particles. In ore dressing studies, physical separation methods, selective grinding, heavy media separation and tabling have been investigated. Obtained results from selective grinding revealed that alumina to silica ratio increases from 1.8 to 1.91 with alumina recovery about 69.3 %. Heavy Liquid separation tests proved that alumina to silica ratio increases to 3.32 with 64.02% alumina recovery by adjusting heavy liquid density to 3.22. Tabling tests approved increase in concentrate module ratio to 2.64 with reduction in alumina recovery to 21%.